PP透明剂，增透剂，聚丙稀，增透母粒

PP nucleating agent

PP透明剂

一、Applicable scope（适用范围）：

PP plastic products.

PP各类塑胶制品。

二、CHARACTERISTICS（特点）：

To improve the transparency and PP plastic products, in the film surface gloss process can reduce the film surface crystal, and make the film surface smoothness, high brightness is better.

提高PP塑胶制品的透明性及表面光泽度，在吹膜过程当中可减少薄膜表面晶点，并使薄膜制品表有平滑度高，光亮度佳的点。

三、TYPICAL PROPERTIES(技术参数)：

The crystallization of PP so fine, uniform and orderly, so that the natural visible light through, so that the transparent polypropylene.

令PP的结晶微细化，均匀且有序，让可见光自然透过，从而使聚丙透明化。

As a very fine crystalline PP and neatly arranged, the product surface is smooth, gloss, stiffness, thermal variations of temperature, tensile strength and creep resistance were increased, so that products gentrification.

由于PP结晶非常微细且整齐排列，产品表面光滑，光泽度、刚性、热变型温度、拉伸强度和抗蠕变性均有提高，令产品化。

Improve the crystallization temperature and crystallization rate of PP, so that rapid cooling molded PP, thereby greatly reducing the machining time and improve production efficiency, reduced production costs.

提高了PP结晶温度和结晶速度，令PP迅速冷却成型，从而大大缩短了产品的加工时间，提高了生产效率，生产成本下降。

四、REGULATORY STATUS（认?）：

SGS test report（检测报告）

五、additive amount（添加）：

1.5-2 %

六、process（使用流程）：

In every 100 kilograms of raw materials to add 1-2 kilograms of PP transparent agent mixture into the blender mixing.

以每一百公斤原料添加1-2公斤的PP透明剂的混合料倒入搅拌机内搅拌均匀。

Using 160 pure, will filter material, mixes good adhesive for 30min blown film, called the initial stage.

采用160目的过滤网,将混好的胶料倒入，连续吹膜30min，此阶段称为初始阶段。

Within 48 hours after the basic clean surface, cannon muzzles, PP transparent film process in this stage are particularly effective, called stable stage, the stage of stable after adding relatively less per 100 kilograms, usually add 1 kg of PP material nucleating agent.

在48小时之后，筒表面本清洗干?，PP透明剂在吹膜过程中的效果特别明显，此阶段称为稳定阶段,稳定阶段后的添加相对比较少，一般是每一百公斤原料添加1公斤的PP透明剂。

七、attention（注意事项）：

In the initial stage of production, the film surface will produce "crystal point or impurity.

在生产的初始阶段，薄膜表面会产生‘晶点’或杂。

Stable stage, the portion of nucleating agent can decrease relatively.

稳定阶段，其透明剂的份可以相对减少。

In the concentration of transparent PP before reach a certain value, PP with concentration of recrystallization temperature increases, more than the value to improve after adding concentration is recrystallization temperature.

透明剂在PP中的浓度达到一定值以前，PP的再结晶温度随浓度增加而增加，超过此值后再增加浓度对提高再结晶温度则无影响。

八、packing（包装）：25kg/bag

九、period of validity（有效期）：

Stored in cool and dry, effective storage period for two years.

储存于阴凉干燥处,有效存储期限为两年。